Aluminum water filter zirconia foam ceramics

Introduction

Foam ceramics are the third generation porous ceramics, which are newly developed after ordinary porous ceramics and honeycomb ceramics. Foam ceramics can form with many twists and turns of numerous tiny holes, which have many advantages such as high strength, high temperature resistance and good filtration and adsorption. They can be widely used in metallurgy, casting, chemical industry, environmental protection, light industry food and energy saving. The porosity is more than 80%, the tensile strength is 2.2MPa, the softening temperature is more than 1500 ℃; the materials are aluminum oxide, magnesium oxide and silicon carbide. The special-shaped products can be prepared according to the needs, with small specific gravity, corrosion resistance and erosion resistance

Main features

Raw material	Alumina	Silicon carbide	Zirconia	Magnesium oxide
Colour	White	Black grey	Yellow	Dark yellow
Pore density	8-60ppi	8-60ppi	8-60ppi	8-60ppi
Porosity	80-90%	80-90%	80-90%	80-90%
Fire resistance	≤1100℃	≤1500℃	≤1700℃	≤1000℃
Bending strength	>0.6Mpa	>0.8Mpa	>1.0Mpa	>0.6Mpa
compressive strength	>0.8Mpa	>0.9Mpa	>1.2Mpa	>0.8Mpa
Bulk density	0.3-0.45g/cm³	0.35-0.5g/cm³	0.9-1.5g/cm³	0.35-0.5g/cm³
Thermal shock resistance	6times/1100℃	6times/1100℃	6times/1100℃	6times/1100℃
Application	Aluminum alloy and others Non ferrous alloys	Ductile iron malleable iron Grey cast iron and other cast iron	A high melting metal alloy, such as steel Alloy steel Stainless steel, etc	Magnesium and high activity alloys

Reference data of flux (10ppi)

Size(mm)	Filter weight (kg)
50×50×22	30
75×50×22	40
75×75×22	60
75×100×22	80
100×100×22	100
Ф50×22	18
Ф80×22	50
Ф90×22	70